Nickel
We bring forth for our clients a comprehensive variety of Nickel , Nickel Rods, Nickel Bars and other Nickel Products. Our products are known around the globe as these are made with International grade raw material, have excellent mechanical & magnetic properties, have high thermal & electrical conductivity which makes them suitable for varied industrial applications. Moreover, our variety is available in various specifications and compositions.
| Specification | ISO Designation | International Equivalent | Chemical Composition by Wt. % | |||||||||||
| EN | CW | ASTM | CIN | Cu% | Ni% | Sn% | Zn% | Mn% | Fe% | Pb% | Imp | |||
| BS 2874 CN102 | CuNi10Fe1Mn | 12163 | 352H | B-121, C-70600 | - | Rem | 10 - 11 | - | - | 0.5 -1 | 1-2 | 0.01 | 0.3max | |
| BS 1400 G3 | CuSn7Ni5Zn3 | - | - | B-505, C-94800 | - | Rem | 5.25 to 5.75 | 6.5 to 7.5 | 1.5 to 3 | - | - | 0.1 to 0.5 | 0.5 | |
| BS 2870 NS 104 | CuNi12Zn24 | 12163 | 403J | B-151, C-75700 | 403J | 63 to 66 | 12 to 13 | - | Rem | 0.2 | - | - | - | |
| Specification | Conditions | Mechanical Properties | Applications | |||
| TS N/mm2 | 0.2PS N/mm2 | E% | Hardness HB |
|||
| BS 2874 CN102 | M | 280 Min | - | 27min | - |
Cupro Nickel alloy, based on copper and Nickel
with Minor addition of Iron and manganese are noted universally for
their particular resistance to with stand sea water corrosion
and erosion. They are used widely in all product forms for heat
exchanger, other water treatment and cooling plant desalination etc. |
| BS 1400 G3 | Unwrought | 340min | 170 | 18 | - |
Application for Nickel Gun Metal are many and
varied, and include engine valve guides, resistance welding equipment
Bearing bushes, Chuk Nuts, Gear Components, motion translation devices,
New application for the alloys outstanding properties are being
continuously developed. |
| BS 2870 NS 104 | Half Hard Temper | 4600 min | - | 8 min | 130 |
This is standard grade for general purpose
applications where the addition a strength of half hard temper material
imparts rigidity and spring properties again the presence of Nickel
provides corrosion and turnish resistance to levels well excess of
normal Brasses material of this temper is still cold workable and
fabricated by bending, punching, stamping etc. |